SpiderBond® LPM 1214B-2 is a thermoplastic hot melt adhesive based on polyamide with good low temperature flexibility, good high temperature stability and low water absorption. It has good adhesion to plastics, metals, paper, fibers, leather and other substrates with a wide range of applications.
LPM 1214B-2 has excellent electrical insulation and flame retardant, and excellent molding performance. It has low viscosity in the molten state, which ensures that it can complete the encapsulation with a low injection pressure and provide good protection for electronic components.
Material properties:
Color | Black | |
Shape | Pellet | |
Density | 0.98±0.05 g/cm³ | |
Softening Point | 170~185°C | Ring and Ball ASTM D 36 |
Melting Viscosity | 210°C 1,000~7,000 cps | LVT Brookfield ASTM D 3236 |
Tensile Strength | 11.5 | ISO 527 |
Yield Strength | 8.5 | ISO 527 |
Elongation at Break | 660% | ISO 527 |
Open Time | 1~10s | ASTM D 4497 |
Glass Transition Temperature (Tg) | -30°C | ASTM D 3111 |
Shore Hardness | 95A/ 43D | Shore A/ Shore D |
Working Temperature | -30°C~140°C |
Form of supply:
Granulate, store in 25 kg or 20 kg net weight bag.
Storage:
Up to max. +35 °C, min. 12 months in original closed container. Be sure that used container are closed immediately with insulation against moisture.
Maybe the adhesive and application properties can decrease by storing with open containers.
Information provided herein is based upon our practical knowledge and experience. Due to different materials used as well as to varying working conditions which are beyond our control we strictly recommend to carry out intensive trials. Any warranty and/or liability shall not be based on above information or personal consultation, except the contents of a consultation is explicitly confirmed by us in writing.
SpiderBond® LPM 1214B-2 is a thermoplastic hot melt adhesive based on polyamide with good low temperature flexibility, good high temperature stability and low water absorption. It has good adhesion to plastics, metals, paper, fibers, leather and other substrates with a wide range of applications.
LPM 1214B-2 has excellent electrical insulation and flame retardant, and excellent molding performance. It has low viscosity in the molten state, which ensures that it can complete the encapsulation with a low injection pressure and provide good protection for electronic components.
Material properties:
Color | Black | |
Shape | Pellet | |
Density | 0.98±0.05 g/cm³ | |
Softening Point | 170~185°C | Ring and Ball ASTM D 36 |
Melting Viscosity | 210°C 1,000~7,000 cps | LVT Brookfield ASTM D 3236 |
Tensile Strength | 11.5 | ISO 527 |
Yield Strength | 8.5 | ISO 527 |
Elongation at Break | 660% | ISO 527 |
Open Time | 1~10s | ASTM D 4497 |
Glass Transition Temperature (Tg) | -30°C | ASTM D 3111 |
Shore Hardness | 95A/ 43D | Shore A/ Shore D |
Working Temperature | -30°C~140°C |
Form of supply:
Granulate, store in 25 kg or 20 kg net weight bag.
Storage:
Up to max. +35 °C, min. 12 months in original closed container. Be sure that used container are closed immediately with insulation against moisture.
Maybe the adhesive and application properties can decrease by storing with open containers.
Information provided herein is based upon our practical knowledge and experience. Due to different materials used as well as to varying working conditions which are beyond our control we strictly recommend to carry out intensive trials. Any warranty and/or liability shall not be based on above information or personal consultation, except the contents of a consultation is explicitly confirmed by us in writing.